OVERVIEW: A 40 year old excess gas bleeder structure had been previously repaired by another contractor. Their coating failed within 2 years. Chemcote was engaged to rectify the faulty repairs with minimal interruption to plant service.
After inspections carried out to identify the extent of the damage, our solution required innovative surface preparation to ensure our coatings have the best opportunity to provide long service life. We delivered the asset owner a result that guarantees many years of protection from fall out and moisture in this aggressive environment.
INDUSTRY
ENVIRONMENT
Very high industrial aggressive areas with fallout from cooling tower
SUBSTRATE
40+ year old mild steel Excess Gas Bleeder structure
CHALLENGE
Plant fall out and moisture from cooling tower nearby, rectify other contractors work and provide long term corrosion solution
SOLUTION
Surface & moisture tolerant Epo-Chem RS 500P and Epo-Chem RA 500M was the ideal solution for this location & environment.
SCOPE
Mechanically clean using needle gun and some other alternative methods behind bolts coupled with specially designed blast nozzels.
Whip abrasive blast and inspect using mirrors
Application of RS 500P @ 100 microns
Check all areas with mirrors and lighting
Application of RA500M in one coat @ 350 microns total DFT
PRODUCTS
OUTCOME
Chemcote’s solution has extended the life of this asset by 12-24 months, and delivered a 30% improvement in functioning. Continuous high performance is guaranteed until our review at the next planned outage.
RELATED CASE STUDIES
Stern Tube Life Extension During Half-life Refit
Patrol boat in slipway for refit Protection against abrasive blasting damage Application of RB364 Tube internal lining complete Overview: The half-life refit of critical components
Air Receiver Restoration for Long-Term Durability
Pitting corrosion near shaft landing After first abrasive blasting After 2nd Abrasive blast holes were found requiring composite reinforcement Filling void in difficult to reach
High Performing Replacement for 316L SS
On inspection flange corrosion Deep pitting on forged section Application of 1st coat Ready to be put into service for 25+ years of life OVERVIEW: