OVERVIEW: The asset owner was looking at extending the life of the condenser tube sheet to prevent galvanic corrosion. We found the water boxes were also experiencing some deterioration. Chemcote were contracted to apply a coating with high insulating properties preventing long term corrosion.
INDUSTRY
Power Generation – Sugar Mill
ENVIRONMENT
40-60°C, brackish / sea water
SUBSTRATE
8 Year Old – Mild Steel water boxes & Stainless Steel tube sheets
CHALLENGE
New tubes were installed in the condenser tube sheet made from an exotic Stainless Steel compared to the low grade tube sheet. We were asked to provide a solution with a coating with a high dielectric strength to prevent the galvanic reaction between dissimilar materials.
SOLUTION
Tube internals were protected by inserting specially designed plastic caps on Inlet/Outlet and Return side of Water Box. This protected the condenser tube sheet.
A glass flake filled vinyl ester was applied to provide excellent permeation resistance and high dielectric strength.
SCOPE
The entire face was hot washed to remove any lubricants and other potential contaminants before abrasive blasting to ensure surface is clean and the correct surface profile is obtained
RB 300 was applied to tube-sheet face, followed by some other areas considered critical, such as the baffle plates, where the existing coating has failed due to under specification
Carried out high voltage spark test beyond Australian Standards to ensure coating integrity
PRODUCTS
Chem-tect™ RB 300 Series, a glass flake filled vinyl ester, provides excellent permeation resistance and high dielectric strength
OUTCOME
The extended life of the coating is expected to exceed 20 years in service, the plant owner is requesting Chemcote to assist further with other corrosion related issues with nearby ancillary equipment.
RELATED CASE STUDIES
22 year old pipes coated with glass flake vinyl ester
Internal lining in excellent condition Abrasive blast externals Recoating of externals Recoating of externals in basement OVERVIEW: The pipes were originally coated internally using
Premature Failure of 316L Stainless Steel Pipes
Severe pitting after 2 months in service After abrasive blasting Damaged internals rebuilt and coated Externally applied caution OVERVIEW: New 316L pipe failed after
Corrosion protection ensures a long life for a new 98% Sulphuric Acid Bund